Styrene-Butadiene Copolymer
Customer Benefits: This SBC is easily processed by injection molding. Molded parts provide excellent part detail on fast production cycles. Molded parts have excellent clarity, good toughness, excellent stiffness, high surface gloss, and can be blended with Polystyrene.
Applications: Garment Hangers
Processing Recommendations:
Melt Temperature: 232°C, maximum. Screw: plasticizing type injection molder more desirable than plunger type molder. Generally no need to dry resin.
Data provided by Chevron Phillips Chemical Company LP.
Chevron Phillips K-Resin® KR99HG Styrene-Butadiene Copolymer, Injection Molding Grade 物性表
物理性能额定值 (公制)额定值 (英制)测试方法
密度 | 1.01 g/cc | 0.0365 lb/in3 | ASTM D792 |
吸水率 | 0.090 % | 0.090 % | ASTM D570 |
熔体流动速率 | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C | 7.5 g/10 min @Load 11.0 lb, Temperature 392 °F | ASTM D1238 |
机械性能额定值 (公制)额定值 (英制)测试方法
肖氏硬度 (邵氏 D) | 65 | 65 | ASTM D2240 |
抗张强度(屈服) | 26.0 MPa | 3770 psi | 2 in per min; ASTM D638; Test specimens were injection molded by ASTM D1897. |
伸长率 (断裂) | 160 % | 160 % | 2 in per min; ASTM D638; Test specimens were injection molded by ASTM D1897. |
弯曲强度 | 34.0 MPa | 4930 psi | Test specimens were injection molded by ASTM D1897; ASTM D790 |
弯曲模量 | 1.413 GPa | 204.9 ksi | Test specimens were injection molded by ASTM D1897; ASTM D790 |
悬壁梁缺口冲击强度 | 0.410 J/cm @Thickness 3.17 mm | 0.768 ft-lb/in @Thickness 0.125 in | ASTM D256 |
冲击试验 | 29.7 J @Thickness 3.17 mm | 21.9 ft-lb @Thickness 0.125 in | Instrumented Total Energy; @ 150 in/sec impact rate; ASTM D3763 |
热性能额定值 (公制)额定值 (英制)测试方法
载荷下热变形温度(1.8 MPa) | 73.0 °C | 163 °F | ASTM D648 |
维卡软化温度 | 87.0 °C | 189 °F | ASTM D1525 |
光学性能额定值 (公制)额定值 (英制)测试方法
Transmission, Visible | 90 % | 90 % | ASTM D1003 |
加工性能额定值 (公制)额定值 (英制)测试方法
加工温度 | <= 232 °C | <= 450 °F |